＼ 代號 Brand
特性質Properties
|
CA-18I |
CA-14IL |
CA-14IM |
CA-14IW |
CA-12IL |
CA-12IM |
CA-12IW |
最高使用溫度 (℃)
Max. Service Temp.
|
1750 |
1400 |
1400 |
1400 |
1200 |
1200 |
1200 |
施工需要量 (T/M3)
Quantity Required
|
1.40 |
1.20 |
1.40 |
1.60 |
1.00 |
1.20 |
1.40 |
添加水量 (%)
Additional Water
|
19∼24 |
40∼50 |
30∼40 |
25∼40 |
40∼60 |
40∼50 |
30∼40 |
體 密 度(g/cm3)
Bulk Density |
110℃×24hrs
( )℃×3hrs |
1.50
1.50
|
1.25
1.15
(1300) |
1.45
1.35
(1300) |
1.65
1.55
(1300) |
1.05
1.00
(1100) |
1.25
1.20
(1100) |
1.45
1.35
(1100) |
耐壓強度 (kg/cm2)
Compressive Strength |
110℃×24hrs
( )℃×3hrs |
50
200
|
80
50
(1300) |
100
50
(1300) |
150
90
(1300) |
30
15
(1100) |
75
35
(1100) |
90
45
(1100) |
抗折強度 (kg/cm2)
Modulus of rupture |
110℃×24hrs
( )℃×3hrs |
10
40
|
15
6
(1300) |
20
8
(1300) |
40
25
(1300) |
10
6
(1100) |
15
6
(1100) |
20
8
(1100) |
再熱變形率 (%) ( )℃×3hrs
Permanent Linear Change |
-0.50
|
-1.0
(1300) |
-0.8
(1300) |
-0.8
(1300) |
-1.2
(1100) |
-1.0
(1100) |
-0.8
(1100) |
熱傳導率(kcal-m.hr.℃)
Thermal Conductivity |
at350℃
at500℃ |
0.85
0.90 |
0.38
0.40 |
0.48
0.48 |
0.60
0.62 |
0.26
0.27 |
0.30
0.32 |
0.46
0.48 |
化學成份 (%)
Chemical Composition |
Al2O3 |
95 |
44 |
46 |
46 |
38 |
40 |
40 |
|
|
＼ 代號 Brand
特性質Properties
|
CA-10IL |
CA-10IM |
CA-10IW |
CA-8IL |
CA-8IM |
CA-8IW |
CA-ISL |
最高使用溫度 (℃)
Max. Service Temp.
|
1000 |
1000 |
1000 |
800 |
800 |
800 |
800 |
施工需要量 (T/M3)
Quantity Required
|
0.80 |
1.00 |
1.20 |
0.60 |
0.80 |
1.00 |
0.40 |
添加水量 (%)
Additional Water
|
45∼65 |
40∼60 |
40∼50 |
50∼65 |
40∼60 |
40∼60 |
50∼70 |
體 密 度(g/cm3)
Bulk Density |
110℃×24hrs
( )℃×3hrs |
0.85
0.80
(900)
|
1.05
0.95
(900) |
1.25
1.15
(900) |
0.65
0.60
(700) |
0.85
0.80
(700) |
1.05
0.95
(700) |
0.45
0.45
(700) |
耐壓強度 (kg/cm2)
Compressive Strength |
110℃×24hrs
( )℃×3hrs |
20
12
(900)
|
30
20
(900) |
60
40
(900) |
10
8
(700) |
20
12
(700) |
30
15
(700) |
6
5
(700) |
抗折強度 (kg/cm2)
Modulus of rupture |
110℃×24hrs
( )℃×3hrs |
8
2
(900) |
10
5
(900) |
15
6
(900) |
5
3
(700) |
8
3
(700) |
10
6
(700) |
3
2
(700) |
再熱變形率 (%) ( )℃×3hrs
Permanent Linear Change |
-0.8
(900)
|
-1.0
(900) |
-0.8
(900) |
-0.8
(700) |
-0.8
(700) |
-0.6
(700) |
-1.0
(700) |
熱傳導率(kcal-m.hr.℃)
Thermal Conductivity |
at350℃
at500℃ |
0.22
0.23 |
0.25
0.27 |
0.29
0.30 |
0.18
0.20 |
0.21
0.22 |
0.24
0.26 |
0.14
0.16 |
化學成份 (%)
Chemical Composition |
Al2O3 |
32 |
35 |
35 |
22 |
24 |
24 |
15 |
|
|
|
|
|
【INSULATING CASTABLES】